English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

The Al-Mg-Ge alloy is one of the age-hardening aluminum alloy after solution heat treatment. It has been proposed that the age-precipitation behavior of Al-Mg-Ge alloy is different from that of Al-Mg-Si alloy according to our previous works about the microstructure on Al-Mg-Ge alloy over-aged at 523K. For example, The hardness of peak aged Al-1.0mass%Mg2Ge alloy is higher than that of Al-1.0mass%Mg2Si alloy. The precipitates in the over-aged samples have been classified as some metastable phases, such as the β’-phase and Type-A precipitates and equilibrium phase of β-Mg2Ge by TEM observation. There a few reports about microstructure on Al-Mg-Ge alloys observed by TEM for different aging times. The age-precipitations structure of Al-Mg-Ge alloy has not been became clear. In this work, TEM observation was investigated the microstructure on Al-1.0mass%Mg2Ge alloy for difference aging times aged at 473K

The Age-Precipitations Structure Of Al-Mg-Ge Alloy Aged At 473K